Product name: CW508L
Main alloying elements: copper (Cu), zinc (Zn)
Mechanical properties:
Tensile strength: 320 - 380 MPa (megapascals)
Yield strength: 160 - 220 MPa
Elongation at break: 35 - 45%
Hardness (Rockwell): -
Modulus of elasticity: 115 - 125 GPa
Physical Properties:
Density: 8.4 g/cm³
Melting point: approx. 900 - 940 °C
Thermal conductivity: 120 - 140 W/(m K)
Electrical conductivity: 40 - 50% IACS (International Annealed Copper Standard)
Chemical composition (in percent by weight):
Copper (Cu): approx. 92 - 95%
Zinc (Zn): approx. 5 - 8%
Heat treatment:
CW508L can be strengthened after casting by various heat treatments such as annealing or work hardening.
Corrosion resistance:
CW508L offers good resistance to corrosion in most atmospheric conditions as well as in fresh water and steam. However, it can be susceptible to corrosion in saline or acidic environments.
Applications:
CW508L is used in a variety of applications including:
Refrigeration technology: heat exchangers, condensers
Plumbing and heating systems: piping, fittings
Electrical engineering: connectors, contacts
General mechanical engineering: gears, plain bearings
Please note that the values given are indicative and may vary slightly depending on the manufacturing process and specific batch. It is recommended to always check the manufacturer's exact specifications.