| element | Mass fraction (%) |
|---|---|
| C | ≤ 0.030 |
| Si | ≤ 1.00 |
| Mn | ≤ 2.00 |
| P | ≤ 0.045 |
| S | ≤ 0.015 |
| Cr | 17.50-19.50 |
| Ni | 9.00-12.00 |
| N | ≤ 0.11 |
| Mechanical properties | Value |
|---|---|
| Tensile strength (Rp0.2) | ≥ 450 MPa |
| Yield strength (Rm) | 650-850 MPa |
| Elongation at break (A5) | ≥ 25% |
| Impact strength (ISO-V) at room temperature | ≥ 100 J |
| Physical properties | Value |
|---|---|
| density | 7.9 g/cm³ |
| Melting point | 1398-1420°C |
| Thermal conductivity (at 20°C) | 15 W/(m·K) |
| Electrical resistance (at 20°C) | 0.73 µΩm |
| Magnetizability (at 20°C) | non-magnetic |
Alloy 1.4306 offers excellent corrosion resistance to oxidizing and non-oxidizing acids and is resistant to pitting and stress corrosion cracking. It is also resistant to atmospheric influences and can be used in saline environments.
The alloy 1.4306 is used in a variety of fields, including:
Please note that technical specifications may vary depending on the alloy composition, manufacturing process, and conditions. The values provided are for guidance only and should not be considered precise.