Technical data sheet for alloy 2.4816:
Chemical composition (in weight percent):
- Nickel (Ni): 72.0 - 75.0%
- Chromium (Cr): 14.0 - 17.0%
- Iron (Fe): max. 7.0%
- Molybdenum (Mo): max. 0.5%
- Carbon (C): max. 0.05%
- Silicon (Si): max. 0.5%
- Manganese (Mn): max. 0.5%
- Sulfur (S): max. 0.015%
- Phosphorus (P): max. 0.02%
Physical properties:
- Density: 8.08 g/cm³
- Melting point: 1,360 - 1,405 °C
- Thermal conductivity: 13.3 W/(m·K)
- Electrical conductivity: 15.5 MS/m
- Magnetizability: non-magnetic
Mechanical properties:
- Tensile strength: min. 500 MPa
- Yield strength: min. 200 MPa
- Elongation at break: min. 35%
- Hardness: max. 215 HB
Corrosion resistance:
- The alloy 2.4816 offers very good corrosion resistance to oxidizing and reducing media, such as air, water, steam, hydrochloric acid, sulfuric acid, nitric acid and acetic acid.
Applications:
- The alloy 2.4816 is used in various applications due to its excellent corrosion resistance, such as in chemical plants, aircraft construction, the nuclear industry, the food industry and the petrochemical industry.
- It is also used for heat exchangers, steam boilers, furnace linings, catalysts and for components in the aerospace industry.
Delivery options:
- Sheet metal
- bars
- Tube
- Fittings
- flanges
- Forged pieces
- wire
Note: The data above is for reference only and may vary depending on the manufacturer and production batch. Always consult the manufacturer's specifications and datasheets before use.